EN 1.4107 Stainless Steel vs. SAE-AISI 1330 Steel
Both EN 1.4107 stainless steel and SAE-AISI 1330 steel are iron alloys. They have 86% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is SAE-AISI 1330 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 18 to 21 | |
11 to 23 |
Fatigue Strength, MPa | 260 to 350 | |
210 to 380 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 76 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 620 to 700 | |
520 to 710 |
Tensile Strength: Yield (Proof), MPa | 400 to 570 | |
290 to 610 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Maximum Temperature: Mechanical, °C | 740 | |
400 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1410 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 27 | |
51 |
Thermal Expansion, µm/m-K | 10 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
7.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
8.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 7.5 | |
1.9 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 2.1 | |
1.4 |
Embodied Energy, MJ/kg | 30 | |
19 |
Embodied Water, L/kg | 100 | |
48 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
76 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 840 | |
230 to 990 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 22 to 25 | |
19 to 25 |
Strength to Weight: Bending, points | 21 to 22 | |
18 to 23 |
Thermal Diffusivity, mm2/s | 7.2 | |
14 |
Thermal Shock Resistance, points | 22 to 25 | |
17 to 23 |
Alloy Composition
Carbon (C), % | 0 to 0.1 | |
0.28 to 0.33 |
Chromium (Cr), % | 11.5 to 12.5 | |
0 |
Copper (Cu), % | 0 to 0.3 | |
0 |
Iron (Fe), % | 83.8 to 87.2 | |
97.3 to 98 |
Manganese (Mn), % | 0.5 to 0.8 | |
1.6 to 1.9 |
Molybdenum (Mo), % | 0 to 0.5 | |
0 |
Nickel (Ni), % | 0.8 to 1.5 | |
0 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.035 |
Silicon (Si), % | 0 to 0.4 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.040 |
Vanadium (V), % | 0 to 0.080 | |
0 |