EN 1.4110 Stainless Steel vs. C14520 Copper
EN 1.4110 stainless steel belongs to the iron alloys classification, while C14520 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4110 stainless steel and the bottom bar is C14520 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 to 14 | |
| 9.0 to 9.6 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 43 |
| Shear Strength, MPa | 470 to 1030 | |
| 170 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1720 | |
| 290 to 330 |
| Tensile Strength: Yield (Proof), MPa | 430 to 1330 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 200 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1080 |
| Melting Onset (Solidus), °C | 1400 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 320 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.8 | |
| 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 85 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 33 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 2.6 |
| Embodied Energy, MJ/kg | 33 | |
| 42 |
| Embodied Water, L/kg | 110 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 180 | |
| 24 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 to 4550 | |
| 240 to 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 28 to 62 | |
| 9.0 to 10 |
| Strength to Weight: Bending, points | 24 to 41 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 94 |
| Thermal Shock Resistance, points | 27 to 60 | |
| 10 to 12 |
Alloy Composition
| Carbon (C), % | 0.48 to 0.6 | |
| 0 |
| Chromium (Cr), % | 13 to 15 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.2 to 99.596 |
| Iron (Fe), % | 81.4 to 86 | |
| 0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.0040 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.4 to 0.7 |
| Vanadium (V), % | 0 to 0.15 | |
| 0 |