EN 1.4110 Stainless Steel vs. C97800 Nickel Silver
EN 1.4110 stainless steel belongs to the iron alloys classification, while C97800 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4110 stainless steel and the bottom bar is C97800 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 130 |
| Elongation at Break, % | 11 to 14 | |
| 10 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 76 | |
| 48 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1720 | |
| 370 |
| Tensile Strength: Yield (Proof), MPa | 430 to 1330 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 230 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1180 |
| Melting Onset (Solidus), °C | 1400 | |
| 1140 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 25 |
| Thermal Expansion, µm/m-K | 11 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.8 | |
| 4.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 4.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 40 |
| Density, g/cm3 | 7.7 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 5.1 |
| Embodied Energy, MJ/kg | 33 | |
| 76 |
| Embodied Water, L/kg | 110 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 180 | |
| 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 to 4550 | |
| 120 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 28 to 62 | |
| 12 |
| Strength to Weight: Bending, points | 24 to 41 | |
| 13 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 7.3 |
| Thermal Shock Resistance, points | 27 to 60 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0.48 to 0.6 | |
| 0 |
| Chromium (Cr), % | 13 to 15 | |
| 0 |
| Copper (Cu), % | 0 | |
| 64 to 67 |
| Iron (Fe), % | 81.4 to 86 | |
| 0 to 1.5 |
| Lead (Pb), % | 0 | |
| 1.0 to 2.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 24 to 27 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 4.0 to 5.5 |
| Vanadium (V), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 1.0 to 4.0 |
| Residuals, % | 0 | |
| 0 to 0.4 |