EN 1.4116 Stainless Steel vs. ASTM A182 Grade FR

Both EN 1.4116 stainless steel and ASTM A182 grade FR are iron alloys. Both are furnished in the annealed condition. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4116 stainless steel and the bottom bar is ASTM A182 grade FR.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14
28
Fatigue Strength, MPa 240
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Shear Strength, MPa 450
320
Tensile Strength: Ultimate (UTS), MPa 750
490
Tensile Strength: Yield (Proof), MPa 430
360

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 800
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
52
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
3.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.5
1.6
Embodied Energy, MJ/kg 36
21
Embodied Water, L/kg 110
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87
120
Resilience: Unit (Modulus of Resilience), kJ/m3 470
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
17
Strength to Weight: Bending, points 24
17
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 26
14

Alloy Composition

Carbon (C), % 0.45 to 0.55
0 to 0.2
Chromium (Cr), % 14 to 15
0
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 81.3 to 85
95.2 to 97.3
Manganese (Mn), % 0 to 1.0
0.4 to 1.1
Molybdenum (Mo), % 0.5 to 0.8
0
Nickel (Ni), % 0
1.6 to 2.2
Nitrogen (N), % 0 to 0.15
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.050
Vanadium (V), % 0.1 to 0.2
0