EN 1.4116 Stainless Steel vs. S44660 Stainless Steel
Both EN 1.4116 stainless steel and S44660 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 82% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.4116 stainless steel and the bottom bar is S44660 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 14 | |
| 20 |
| Fatigue Strength, MPa | 240 | |
| 330 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Rockwell B Hardness | 88 | |
| 88 |
| Shear Modulus, GPa | 76 | |
| 81 |
| Shear Strength, MPa | 450 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 750 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 640 |
| Maximum Temperature: Mechanical, °C | 800 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 17 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.1 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 21 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 4.3 |
| Embodied Energy, MJ/kg | 36 | |
| 61 |
| Embodied Water, L/kg | 110 | |
| 180 |
Common Calculations
| PREN (Pitting Resistance) | 18 | |
| 38 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 | |
| 640 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 27 | |
| 24 |
| Strength to Weight: Bending, points | 24 | |
| 22 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 4.5 |
| Thermal Shock Resistance, points | 26 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0.45 to 0.55 | |
| 0 to 0.030 |
| Chromium (Cr), % | 14 to 15 | |
| 25 to 28 |
| Iron (Fe), % | 81.3 to 85 | |
| 60.4 to 71 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 3.0 to 4.0 |
| Nickel (Ni), % | 0 | |
| 1.0 to 3.5 |
| Niobium (Nb), % | 0 | |
| 0.2 to 1.0 |
| Nitrogen (N), % | 0 to 0.15 | |
| 0 to 0.040 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.2 to 1.0 |
| Vanadium (V), % | 0.1 to 0.2 | |
| 0 |