EN 1.4122 Stainless Steel vs. EN 1.7230 Steel

Both EN 1.4122 stainless steel and EN 1.7230 steel are iron alloys. They have 83% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4122 stainless steel and the bottom bar is EN 1.7230 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14
11 to 12
Fatigue Strength, MPa 260 to 360
320 to 460
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 790 to 850
720 to 910
Tensile Strength: Yield (Proof), MPa 450 to 630
510 to 740

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.4
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.4
1.5
Embodied Energy, MJ/kg 33
20
Embodied Water, L/kg 120
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 110
79 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 520 to 1000
700 to 1460
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28 to 31
26 to 32
Strength to Weight: Bending, points 25 to 26
23 to 27
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 28 to 30
21 to 27

Alloy Composition

Carbon (C), % 0.33 to 0.45
0.3 to 0.37
Chromium (Cr), % 15.5 to 17.5
0.8 to 1.2
Iron (Fe), % 77.2 to 83.4
96.7 to 98.3
Manganese (Mn), % 0 to 1.5
0.5 to 0.8
Molybdenum (Mo), % 0.8 to 1.3
0.15 to 0.3
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.030