EN 1.4122 Stainless Steel vs. R31538 Cobalt

EN 1.4122 stainless steel belongs to the iron alloys classification, while R31538 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4122 stainless steel and the bottom bar is R31538 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 14
13 to 23
Fatigue Strength, MPa 260 to 360
310 to 480
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
86
Tensile Strength: Ultimate (UTS), MPa 790 to 850
1020 to 1360
Tensile Strength: Yield (Proof), MPa 450 to 630
580 to 930

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Melting Completion (Liquidus), °C 1440
1360
Melting Onset (Solidus), °C 1400
1290
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.1

Otherwise Unclassified Properties

Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 2.4
8.1
Embodied Energy, MJ/kg 33
110
Embodied Water, L/kg 120
530

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 110
140 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 520 to 1000
750 to 1920
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28 to 31
34 to 45
Strength to Weight: Bending, points 25 to 26
27 to 32
Thermal Diffusivity, mm2/s 4.0
3.5
Thermal Shock Resistance, points 28 to 30
25 to 33

Alloy Composition

Carbon (C), % 0.33 to 0.45
0.15 to 0.35
Chromium (Cr), % 15.5 to 17.5
26 to 30
Cobalt (Co), % 0
58.7 to 68.9
Iron (Fe), % 77.2 to 83.4
0 to 0.75
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0.8 to 1.3
5.0 to 7.0
Nickel (Ni), % 0 to 1.0
0 to 1.0
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0

Comparable Variants