EN 1.4122 Stainless Steel vs. Type 3 Magnetic Alloy
EN 1.4122 stainless steel belongs to the iron alloys classification, while Type 3 magnetic alloy belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4122 stainless steel and the bottom bar is Type 3 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 180 |
| Elongation at Break, % | 14 | |
| 43 |
| Fatigue Strength, MPa | 260 to 360 | |
| 170 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 70 |
| Shear Strength, MPa | 480 to 520 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 850 | |
| 550 |
| Tensile Strength: Yield (Proof), MPa | 450 to 630 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 910 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1370 |
| Melting Onset (Solidus), °C | 1400 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 3.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 55 |
| Density, g/cm3 | 7.7 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 8.7 |
| Embodied Energy, MJ/kg | 33 | |
| 120 |
| Embodied Water, L/kg | 120 | |
| 220 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 93 to 110 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 520 to 1000 | |
| 120 |
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 28 to 31 | |
| 18 |
| Strength to Weight: Bending, points | 25 to 26 | |
| 17 |
| Thermal Shock Resistance, points | 28 to 30 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.33 to 0.45 | |
| 0 to 0.050 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 2.0 to 3.0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 | |
| 4.0 to 6.0 |
| Iron (Fe), % | 77.2 to 83.4 | |
| 9.9 to 19 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.8 to 1.3 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 75 to 78 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.020 |