EN 1.4150 Stainless Steel vs. ASTM A182 Grade F5

Both EN 1.4150 stainless steel and ASTM A182 grade F5 are iron alloys. Both are furnished in the annealed condition. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4150 stainless steel and the bottom bar is ASTM A182 grade F5.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
22
Fatigue Strength, MPa 270
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Shear Strength, MPa 460
340
Tensile Strength: Ultimate (UTS), MPa 730
540
Tensile Strength: Yield (Proof), MPa 430
310

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 840
510
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 23
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
4.5
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.8
Embodied Energy, MJ/kg 42
24
Embodied Water, L/kg 120
69

Common Calculations

PREN (Pitting Resistance) 19
6.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
100
Resilience: Unit (Modulus of Resilience), kJ/m3 470
260
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
19
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 6.2
11
Thermal Shock Resistance, points 27
15

Alloy Composition

Carbon (C), % 0.45 to 0.6
0 to 0.15
Chromium (Cr), % 15 to 16.5
4.0 to 6.0
Iron (Fe), % 79 to 82.8
91.5 to 95.3
Manganese (Mn), % 0 to 0.8
0.3 to 0.6
Molybdenum (Mo), % 0.2 to 0.4
0.44 to 0.65
Nickel (Ni), % 0 to 0.4
0 to 0.5
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 1.3 to 1.7
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Vanadium (V), % 0.2 to 0.4
0