EN 1.4150 Stainless Steel vs. SAE-AISI H14 Steel

Both EN 1.4150 stainless steel and SAE-AISI H14 steel are iron alloys. They have 88% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4150 stainless steel and the bottom bar is SAE-AISI H14 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
75
Tensile Strength: Ultimate (UTS), MPa 730
710 to 2030

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1420
1530
Melting Onset (Solidus), °C 1380
1490
Specific Heat Capacity, J/kg-K 490
460
Thermal Conductivity, W/m-K 23
35
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
15
Density, g/cm3 7.6
8.1
Embodied Carbon, kg CO2/kg material 2.8
2.7
Embodied Energy, MJ/kg 42
39
Embodied Water, L/kg 120
73

Common Calculations

PREN (Pitting Resistance) 19
13
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
24 to 69
Strength to Weight: Bending, points 24
22 to 44
Thermal Diffusivity, mm2/s 6.2
9.3
Thermal Shock Resistance, points 27
24 to 68

Alloy Composition

Carbon (C), % 0.45 to 0.6
0.35 to 0.45
Chromium (Cr), % 15 to 16.5
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 79 to 82.8
86.5 to 89.9
Manganese (Mn), % 0 to 0.8
0.2 to 0.5
Molybdenum (Mo), % 0.2 to 0.4
0
Nickel (Ni), % 0 to 0.4
0 to 0.3
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 1.3 to 1.7
0.8 to 1.2
Sulfur (S), % 0 to 0.010
0 to 0.030
Tungsten (W), % 0
4.0 to 5.3
Vanadium (V), % 0.2 to 0.4
0