EN 1.4307 Stainless Steel vs. EN 1.4913 Stainless Steel

Both EN 1.4307 stainless steel and EN 1.4913 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 1.4913 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 46
14 to 22
Fatigue Strength, MPa 190 to 320
320 to 480
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Shear Strength, MPa 410 to 550
550 to 590
Tensile Strength: Ultimate (UTS), MPa 590 to 900
870 to 980
Tensile Strength: Yield (Proof), MPa 200 to 570
480 to 850

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 940
700
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
24
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
9.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
2.9
Embodied Energy, MJ/kg 43
41
Embodied Water, L/kg 140
97

Common Calculations

PREN (Pitting Resistance) 19
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
130 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
600 to 1860
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
31 to 35
Strength to Weight: Bending, points 20 to 27
26 to 28
Thermal Diffusivity, mm2/s 4.0
6.5
Thermal Shock Resistance, points 13 to 20
31 to 34

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0 to 0.0015
Carbon (C), % 0 to 0.030
0.17 to 0.23
Chromium (Cr), % 17.5 to 19.5
10 to 11.5
Iron (Fe), % 66.8 to 74.5
84.5 to 88.3
Manganese (Mn), % 0 to 2.0
0.4 to 0.9
Molybdenum (Mo), % 0
0.5 to 0.8
Nickel (Ni), % 8.0 to 10.5
0.2 to 0.6
Niobium (Nb), % 0
0.25 to 0.55
Nitrogen (N), % 0 to 0.1
0.050 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015
Vanadium (V), % 0
0.1 to 0.3

Comparable Variants