EN 1.4307 Stainless Steel vs. C92700 Bronze
EN 1.4307 stainless steel belongs to the iron alloys classification, while C92700 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is C92700 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 14 to 46 | |
| 9.1 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 900 | |
| 290 |
| Tensile Strength: Yield (Proof), MPa | 200 to 570 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 940 | |
| 170 |
| Melting Completion (Liquidus), °C | 1430 | |
| 980 |
| Melting Onset (Solidus), °C | 1380 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 370 |
| Thermal Conductivity, W/m-K | 15 | |
| 47 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 35 |
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.6 |
| Embodied Energy, MJ/kg | 43 | |
| 58 |
| Embodied Water, L/kg | 140 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 210 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 810 | |
| 110 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 21 to 32 | |
| 9.1 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 11 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 15 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 17.5 to 19.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 86 to 89 |
| Iron (Fe), % | 66.8 to 74.5 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 1.0 to 2.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 8.0 to 10.5 | |
| 0 to 1.0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 9.0 to 11 |
| Zinc (Zn), % | 0 | |
| 0 to 0.7 |
| Residuals, % | 0 | |
| 0 to 0.7 |