EN 1.4308 Stainless Steel vs. EN 1.4876 Stainless Steel

Both EN 1.4308 stainless steel and EN 1.4876 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is EN 1.4876 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
33
Fatigue Strength, MPa 160
150
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 510
570
Tensile Strength: Yield (Proof), MPa 200
190

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 420
490
Maximum Temperature: Mechanical, °C 960
1100
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1380
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.0
5.3
Embodied Energy, MJ/kg 43
76
Embodied Water, L/kg 150
200

Common Calculations

PREN (Pitting Resistance) 19
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
140
Resilience: Unit (Modulus of Resilience), kJ/m3 100
94
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.1
3.2
Thermal Shock Resistance, points 11
14

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.070
0 to 0.12
Chromium (Cr), % 18 to 20
19 to 23
Iron (Fe), % 65.9 to 74
38.6 to 50.7
Manganese (Mn), % 0 to 1.5
0 to 2.0
Nickel (Ni), % 8.0 to 11
30 to 34
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6