EN 1.4308 Stainless Steel vs. S35315 Stainless Steel

Both EN 1.4308 stainless steel and S35315 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is S35315 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
46
Fatigue Strength, MPa 160
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 510
740
Tensile Strength: Yield (Proof), MPa 200
300

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Maximum Temperature: Corrosion, °C 420
450
Maximum Temperature: Mechanical, °C 960
1100
Melting Completion (Liquidus), °C 1420
1370
Melting Onset (Solidus), °C 1380
1330
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 15
34
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
5.7
Embodied Energy, MJ/kg 43
81
Embodied Water, L/kg 150
220

Common Calculations

PREN (Pitting Resistance) 19
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
270
Resilience: Unit (Modulus of Resilience), kJ/m3 100
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.1
3.1
Thermal Shock Resistance, points 11
17

Alloy Composition

Carbon (C), % 0 to 0.070
0.040 to 0.080
Cerium (Ce), % 0
0.030 to 0.1
Chromium (Cr), % 18 to 20
24 to 26
Iron (Fe), % 65.9 to 74
33.6 to 40.6
Manganese (Mn), % 0 to 1.5
0 to 2.0
Nickel (Ni), % 8.0 to 11
34 to 36
Nitrogen (N), % 0
0.12 to 0.18
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
1.2 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.030