EN 1.4309 Stainless Steel vs. AWS E90C-B9

Both EN 1.4309 stainless steel and AWS E90C-B9 are iron alloys. They have 79% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4309 stainless steel and the bottom bar is AWS E90C-B9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
18
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 490
710
Tensile Strength: Yield (Proof), MPa 210
460

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 16
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
2.6
Embodied Energy, MJ/kg 45
37
Embodied Water, L/kg 150
91

Common Calculations

PREN (Pitting Resistance) 21
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 110
550
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
25
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.1
6.9
Thermal Shock Resistance, points 11
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.030
0.080 to 0.13
Chromium (Cr), % 18 to 20
8.0 to 10.5
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 64.2 to 73
84.4 to 90.9
Manganese (Mn), % 0 to 2.0
0 to 1.2
Molybdenum (Mo), % 0
0.85 to 1.2
Nickel (Ni), % 9.0 to 12
0 to 0.8
Niobium (Nb), % 0
0.020 to 0.1
Nitrogen (N), % 0 to 0.2
0.030 to 0.070
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0
0.15 to 0.3
Residuals, % 0
0 to 0.5