EN 1.4309 Stainless Steel vs. EN 1.4600 Stainless Steel

Both EN 1.4309 stainless steel and EN 1.4600 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4309 stainless steel and the bottom bar is EN 1.4600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Fatigue Strength, MPa 170
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 490
580
Tensile Strength: Yield (Proof), MPa 210
430

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 960
730
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
27
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 16
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.1
2.0
Embodied Energy, MJ/kg 45
28
Embodied Water, L/kg 150
100

Common Calculations

PREN (Pitting Resistance) 21
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 110
470
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.1
7.3
Thermal Shock Resistance, points 11
21

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
11 to 13
Iron (Fe), % 64.2 to 73
82 to 87.7
Manganese (Mn), % 0 to 2.0
1.0 to 2.5
Nickel (Ni), % 9.0 to 12
0.3 to 1.0
Nitrogen (N), % 0 to 0.2
0 to 0.025
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0 to 0.35