EN 1.4310 Stainless Steel vs. AWS BAg-18

EN 1.4310 stainless steel belongs to the iron alloys classification, while AWS BAg-18 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is AWS BAg-18.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
82
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 77
30
Tensile Strength: Ultimate (UTS), MPa 730 to 900
170

Thermal Properties

Latent Heat of Fusion, J/g 290
130
Melting Completion (Liquidus), °C 1420
720
Melting Onset (Solidus), °C 1380
600
Specific Heat Capacity, J/kg-K 480
280
Thermal Expansion, µm/m-K 18
19

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.7
Embodied Carbon, kg CO2/kg material 2.9
59
Embodied Energy, MJ/kg 42
930

Common Calculations

Stiffness to Weight: Axial, points 14
4.7
Stiffness to Weight: Bending, points 25
15
Strength to Weight: Axial, points 26 to 32
4.9
Strength to Weight: Bending, points 23 to 27
7.0
Thermal Shock Resistance, points 15 to 18
7.7

Alloy Composition

Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 16 to 19
0
Copper (Cu), % 0
28.4 to 31.5
Iron (Fe), % 66.4 to 78
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.8
0
Nickel (Ni), % 6.0 to 9.5
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 2.0
0
Silver (Ag), % 0
59 to 61
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
9.5 to 10.5
Residuals, % 0
0 to 0.15