EN 1.4310 Stainless Steel vs. AWS E2209
Both EN 1.4310 stainless steel and AWS E2209 are iron alloys. They have 90% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is AWS E2209.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 14 to 45 | |
| 23 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 900 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 300 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1440 |
| Melting Onset (Solidus), °C | 1380 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 16 |
| Thermal Expansion, µm/m-K | 18 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 20 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 4.0 |
| Embodied Energy, MJ/kg | 42 | |
| 55 |
| Embodied Water, L/kg | 140 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 35 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 27 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 24 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.3 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.040 |
| Chromium (Cr), % | 16 to 19 | |
| 21.5 to 23.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 66.4 to 78 | |
| 58.4 to 66.9 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.5 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.8 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 6.0 to 9.5 | |
| 8.5 to 10.5 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0.080 to 0.2 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |