EN 1.4310 Stainless Steel vs. AWS E308Mo

Both EN 1.4310 stainless steel and AWS E308Mo are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is AWS E308Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 45
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 730 to 900
620

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 18
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 14
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.9
3.8
Embodied Energy, MJ/kg 42
53
Embodied Water, L/kg 140
160

Common Calculations

PREN (Pitting Resistance) 20
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26 to 32
22
Strength to Weight: Bending, points 23 to 27
20
Thermal Diffusivity, mm2/s 4.0
4.2
Thermal Shock Resistance, points 15 to 18
16

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.080
Chromium (Cr), % 16 to 19
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 66.4 to 78
59.6 to 70.5
Manganese (Mn), % 0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.8
2.0 to 3.0
Nickel (Ni), % 6.0 to 9.5
9.0 to 12
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030