EN 1.4310 Stainless Steel vs. SAE-AISI 1330 Steel

Both EN 1.4310 stainless steel and SAE-AISI 1330 steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is SAE-AISI 1330 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 270
150 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 45
11 to 23
Fatigue Strength, MPa 240 to 330
210 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 510 to 550
330 to 430
Tensile Strength: Ultimate (UTS), MPa 730 to 900
520 to 710
Tensile Strength: Yield (Proof), MPa 260 to 570
290 to 610

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 910
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 14
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.4
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 140
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 260
76 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 830
230 to 990
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26 to 32
19 to 25
Strength to Weight: Bending, points 23 to 27
18 to 23
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 15 to 18
17 to 23

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.28 to 0.33
Chromium (Cr), % 16 to 19
0
Iron (Fe), % 66.4 to 78
97.3 to 98
Manganese (Mn), % 0 to 2.0
1.6 to 1.9
Molybdenum (Mo), % 0 to 0.8
0
Nickel (Ni), % 6.0 to 9.5
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 2.0
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040

Comparable Variants