EN 1.4310 Stainless Steel vs. N06045 Nickel
EN 1.4310 stainless steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have 50% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is N06045 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 14 to 45 | |
| 37 |
| Fatigue Strength, MPa | 240 to 330 | |
| 210 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Shear Strength, MPa | 510 to 550 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 900 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 260 to 570 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1350 |
| Melting Onset (Solidus), °C | 1380 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 42 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 6.9 |
| Embodied Energy, MJ/kg | 42 | |
| 98 |
| Embodied Water, L/kg | 140 | |
| 250 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 28 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 260 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 830 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 24 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 22 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0.050 to 0.12 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.090 |
| Chromium (Cr), % | 16 to 19 | |
| 26 to 29 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 66.4 to 78 | |
| 21 to 25 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.8 | |
| 0 |
| Nickel (Ni), % | 6.0 to 9.5 | |
| 45 to 50.4 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 2.0 | |
| 2.5 to 3.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |