EN 1.4310 Stainless Steel vs. N07041 Nickel
EN 1.4310 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 14 to 45 | |
| 14 |
| Fatigue Strength, MPa | 240 to 330 | |
| 540 |
| Shear Strength, MPa | 510 to 550 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 900 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 260 to 570 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1380 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 15 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 260 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 830 | |
| 2510 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 47 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 34 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 3.0 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 38 |