EN 1.4313 Stainless Steel vs. EN 1.7711 Steel
Both EN 1.4313 stainless steel and EN 1.7711 steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4313 stainless steel and the bottom bar is EN 1.7711 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 12 to 17 | |
| 16 to 22 |
| Fatigue Strength, MPa | 340 to 510 | |
| 290 to 520 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 460 to 600 | |
| 440 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 750 to 1000 | |
| 690 to 930 |
| Tensile Strength: Yield (Proof), MPa | 580 to 910 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 780 | |
| 430 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 25 | |
| 33 |
| Thermal Expansion, µm/m-K | 10 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 3.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 2.3 |
| Embodied Energy, MJ/kg | 34 | |
| 32 |
| Embodied Water, L/kg | 110 | |
| 54 |
Common Calculations
| PREN (Pitting Resistance) | 15 | |
| 2.9 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
| 130 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 870 to 2100 | |
| 430 to 1690 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 27 to 36 | |
| 24 to 33 |
| Strength to Weight: Bending, points | 23 to 28 | |
| 22 to 27 |
| Thermal Diffusivity, mm2/s | 6.7 | |
| 8.9 |
| Thermal Shock Resistance, points | 27 to 36 | |
| 24 to 32 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 to 0.050 | |
| 0.36 to 0.44 |
| Chromium (Cr), % | 12 to 14 | |
| 0.9 to 1.2 |
| Iron (Fe), % | 78.5 to 84.2 | |
| 96 to 97.5 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.45 to 0.85 |
| Molybdenum (Mo), % | 0.3 to 0.7 | |
| 0.5 to 0.65 |
| Nickel (Ni), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |