EN 1.4315 Stainless Steel vs. EN 1.8819 Steel

Both EN 1.4315 stainless steel and EN 1.8819 steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4315 stainless steel and the bottom bar is EN 1.8819 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
27
Fatigue Strength, MPa 290
200
Impact Strength: V-Notched Charpy, J 90
49
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 440
280
Tensile Strength: Ultimate (UTS), MPa 630
440
Tensile Strength: Yield (Proof), MPa 310
270

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 960
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
48
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.6
Embodied Energy, MJ/kg 43
21
Embodied Water, L/kg 150
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
100
Resilience: Unit (Modulus of Resilience), kJ/m3 240
190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
16
Strength to Weight: Bending, points 21
16
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.034
Carbon (C), % 0 to 0.060
0 to 0.15
Chromium (Cr), % 18 to 20
0 to 0.35
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 65.7 to 73.9
95.9 to 99.985
Manganese (Mn), % 0 to 2.0
0 to 1.6
Molybdenum (Mo), % 0
0 to 0.13
Nickel (Ni), % 8.0 to 11
0 to 0.35
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0.12 to 0.22
0 to 0.017
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.1