EN 1.4325 Stainless Steel vs. ACI-ASTM CK20 Steel

Both EN 1.4325 stainless steel and ACI-ASTM CK20 steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4325 stainless steel and the bottom bar is ACI-ASTM CK20 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
37
Fatigue Strength, MPa 190
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 650
530
Tensile Strength: Yield (Proof), MPa 210
260

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Corrosion, °C 410
440
Maximum Temperature: Mechanical, °C 930
1100
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
14
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
4.4
Embodied Energy, MJ/kg 42
62
Embodied Water, L/kg 140
190

Common Calculations

PREN (Pitting Resistance) 18
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
160
Resilience: Unit (Modulus of Resilience), kJ/m3 110
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 4.3
3.7
Thermal Shock Resistance, points 15
13

Alloy Composition

Carbon (C), % 0.030 to 0.15
0 to 0.2
Chromium (Cr), % 17 to 19
23 to 27
Iron (Fe), % 67.8 to 75
46.7 to 58
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 8.0 to 10
19 to 22
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040