EN 1.4325 Stainless Steel vs. SAE-AISI M50 Steel

Both EN 1.4325 stainless steel and SAE-AISI M50 steel are iron alloys. They have 77% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4325 stainless steel and the bottom bar is SAE-AISI M50 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 650
720 to 2250

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Melting Completion (Liquidus), °C 1430
1480
Melting Onset (Solidus), °C 1380
1440
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
35
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 15
9.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
5.1
Embodied Energy, MJ/kg 42
74
Embodied Water, L/kg 140
83

Common Calculations

PREN (Pitting Resistance) 18
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
26 to 80
Strength to Weight: Bending, points 21
23 to 49
Thermal Diffusivity, mm2/s 4.3
9.7
Thermal Shock Resistance, points 15
21 to 66

Alloy Composition

Carbon (C), % 0.030 to 0.15
0.78 to 0.88
Chromium (Cr), % 17 to 19
3.8 to 4.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 67.8 to 75
87 to 90.4
Manganese (Mn), % 0 to 2.0
0.15 to 0.45
Molybdenum (Mo), % 0
3.9 to 4.8
Nickel (Ni), % 8.0 to 10
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.8 to 1.3