EN 1.4325 Stainless Steel vs. S35125 Stainless Steel

Both EN 1.4325 stainless steel and S35125 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4325 stainless steel and the bottom bar is S35125 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
39
Fatigue Strength, MPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 450
370
Tensile Strength: Ultimate (UTS), MPa 650
540
Tensile Strength: Yield (Proof), MPa 210
230

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 410
490
Maximum Temperature: Mechanical, °C 930
1100
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.0
6.4
Embodied Energy, MJ/kg 42
89
Embodied Water, L/kg 140
210

Common Calculations

PREN (Pitting Resistance) 18
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
170
Resilience: Unit (Modulus of Resilience), kJ/m3 110
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
19
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 4.3
3.1
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0.030 to 0.15
0 to 0.1
Chromium (Cr), % 17 to 19
20 to 23
Iron (Fe), % 67.8 to 75
36.2 to 45.8
Manganese (Mn), % 0 to 2.0
1.0 to 1.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 8.0 to 10
31 to 35
Niobium (Nb), % 0
0.25 to 0.6
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015