EN 1.4361 Stainless Steel vs. AWS BAg-37

EN 1.4361 stainless steel belongs to the iron alloys classification, while AWS BAg-37 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is EN 1.4361 stainless steel and the bottom bar is AWS BAg-37.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
94
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 75
36
Tensile Strength: Ultimate (UTS), MPa 630
180

Thermal Properties

Latent Heat of Fusion, J/g 350
150
Melting Completion (Liquidus), °C 1370
780
Melting Onset (Solidus), °C 1330
690
Specific Heat Capacity, J/kg-K 490
350
Thermal Expansion, µm/m-K 16
21

Otherwise Unclassified Properties

Density, g/cm3 7.6
8.5
Embodied Carbon, kg CO2/kg material 3.6
26
Embodied Energy, MJ/kg 52
410

Common Calculations

Stiffness to Weight: Axial, points 14
6.1
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 23
5.9
Strength to Weight: Bending, points 21
8.3
Thermal Shock Resistance, points 15
6.6

Alloy Composition

Carbon (C), % 0 to 0.015
0
Chromium (Cr), % 16.5 to 18.5
0
Copper (Cu), % 0
39 to 41
Iron (Fe), % 58.7 to 65.8
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 16
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 3.7 to 4.5
0
Silver (Ag), % 0
24 to 26
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
1.5 to 2.5
Zinc (Zn), % 0
31 to 35
Residuals, % 0
0 to 0.15