EN 1.4361 Stainless Steel vs. EN 1.5511 Steel

Both EN 1.4361 stainless steel and EN 1.5511 steel are iron alloys. They have 63% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4361 stainless steel and the bottom bar is EN 1.5511 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
150 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 630
490 to 580

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.4
Embodied Energy, MJ/kg 52
19
Embodied Water, L/kg 150
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
17 to 20
Strength to Weight: Bending, points 21
18 to 20
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 15
15 to 17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.015
0.32 to 0.39
Chromium (Cr), % 16.5 to 18.5
0
Iron (Fe), % 58.7 to 65.8
98.3 to 99.159
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 16
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 3.7 to 4.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.015