EN 1.4361 Stainless Steel vs. Z24311 Zinc

EN 1.4361 stainless steel belongs to the iron alloys classification, while Z24311 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4361 stainless steel and the bottom bar is Z24311 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 43
63
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 75
35
Tensile Strength: Ultimate (UTS), MPa 630
140
Tensile Strength: Yield (Proof), MPa 250
120

Thermal Properties

Latent Heat of Fusion, J/g 350
110
Maximum Temperature: Mechanical, °C 940
90
Melting Completion (Liquidus), °C 1370
410
Melting Onset (Solidus), °C 1330
400
Specific Heat Capacity, J/kg-K 490
390
Thermal Conductivity, W/m-K 14
110
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
37

Otherwise Unclassified Properties

Base Metal Price, % relative 19
11
Density, g/cm3 7.6
6.6
Embodied Carbon, kg CO2/kg material 3.6
2.8
Embodied Energy, MJ/kg 52
53
Embodied Water, L/kg 150
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
85
Resilience: Unit (Modulus of Resilience), kJ/m3 160
81
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 23
6.1
Strength to Weight: Bending, points 21
9.3
Thermal Diffusivity, mm2/s 3.7
44
Thermal Shock Resistance, points 15
4.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.015
0
Chromium (Cr), % 16.5 to 18.5
0
Copper (Cu), % 0
0 to 0.0050
Iron (Fe), % 58.7 to 65.8
0 to 0.010
Lead (Pb), % 0
0.030 to 0.080
Magnesium (Mg), % 0
0 to 0.0015
Manganese (Mn), % 0 to 2.0
0 to 0.015
Molybdenum (Mo), % 0 to 0.2
0
Nickel (Ni), % 14 to 16
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 3.7 to 4.5
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
99.862 to 100