EN 1.4362 Stainless Steel vs. N08926 Stainless Steel

Both EN 1.4362 stainless steel and N08926 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4362 stainless steel and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
40
Fatigue Strength, MPa 320
290
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
80
Shear Strength, MPa 470
500
Tensile Strength: Ultimate (UTS), MPa 730
740
Tensile Strength: Yield (Proof), MPa 460
330

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 1060
1100
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 14
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.9
6.2
Embodied Energy, MJ/kg 41
84
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 26
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
240
Resilience: Unit (Modulus of Resilience), kJ/m3 530
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
25
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 4.0
3.2
Thermal Shock Resistance, points 20
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 22 to 24.5
19 to 21
Copper (Cu), % 0.1 to 0.6
0.5 to 1.5
Iron (Fe), % 65.5 to 74.3
41.7 to 50.4
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0.1 to 0.6
6.0 to 7.0
Nickel (Ni), % 3.5 to 5.5
24 to 26
Nitrogen (N), % 0.050 to 0.2
0.15 to 0.25
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010