EN 1.4371 Stainless Steel vs. Grade 20 Titanium
EN 1.4371 stainless steel belongs to the iron alloys classification, while grade 20 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4371 stainless steel and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 45 to 51 | |
| 5.7 to 17 |
| Fatigue Strength, MPa | 290 to 340 | |
| 550 to 630 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 47 |
| Shear Strength, MPa | 520 to 540 | |
| 560 to 740 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 750 | |
| 900 to 1270 |
| Tensile Strength: Yield (Proof), MPa | 320 to 340 | |
| 850 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 370 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1660 |
| Melting Onset (Solidus), °C | 1370 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 520 |
| Thermal Expansion, µm/m-K | 17 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 52 |
| Embodied Energy, MJ/kg | 38 | |
| 860 |
| Embodied Water, L/kg | 140 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 to 310 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 300 | |
| 2940 to 5760 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 33 |
| Strength to Weight: Axial, points | 27 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 24 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 16 | |
| 55 to 77 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.050 |
| Chromium (Cr), % | 16 to 17.5 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 66.7 to 74.4 | |
| 0 to 0.3 |
| Manganese (Mn), % | 6.0 to 8.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.25 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |