EN 1.4372 Stainless Steel vs. ACI-ASTM CC50 Steel
Both EN 1.4372 stainless steel and ACI-ASTM CC50 steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4372 stainless steel and the bottom bar is ACI-ASTM CC50 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 77 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 460 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1420 |
| Melting Onset (Solidus), °C | 1370 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 490 |
| Thermal Conductivity, W/m-K | 15 | |
| 17 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 14 |
| Density, g/cm3 | 7.7 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 38 | |
| 39 |
| Embodied Water, L/kg | 140 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 28 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 29 | |
| 16 |
| Strength to Weight: Bending, points | 25 | |
| 17 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.5 |
| Thermal Shock Resistance, points | 17 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.5 |
| Chromium (Cr), % | 16 to 18 | |
| 26 to 30 |
| Iron (Fe), % | 67.5 to 75 | |
| 62.9 to 74 |
| Manganese (Mn), % | 5.5 to 7.5 | |
| 0 to 1.0 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 0 to 4.0 |
| Nitrogen (N), % | 0.050 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.040 |