EN 1.4372 Stainless Steel vs. EN 1.4825 Stainless Steel

Both EN 1.4372 stainless steel and EN 1.4825 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4372 stainless steel and the bottom bar is EN 1.4825 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 47
17
Fatigue Strength, MPa 330
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 790
510
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 880
900
Melting Completion (Liquidus), °C 1410
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
15
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.6
3.1
Embodied Energy, MJ/kg 38
43
Embodied Water, L/kg 140
140

Common Calculations

PREN (Pitting Resistance) 19
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 310
72
Resilience: Unit (Modulus of Resilience), kJ/m3 320
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 17
12

Alloy Composition

Carbon (C), % 0 to 0.15
0.15 to 0.35
Chromium (Cr), % 16 to 18
17 to 19
Iron (Fe), % 67.5 to 75
65.6 to 74.4
Manganese (Mn), % 5.5 to 7.5
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 3.5 to 5.5
8.0 to 10
Nitrogen (N), % 0.050 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0.5 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030