EN 1.4372 Stainless Steel vs. SAE-AISI P4 Steel

Both EN 1.4372 stainless steel and SAE-AISI P4 steel are iron alloys. They have 77% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4372 stainless steel and the bottom bar is SAE-AISI P4 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 790
390 to 1980

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
41
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
4.4
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.8
Embodied Energy, MJ/kg 38
23
Embodied Water, L/kg 140
68

Common Calculations

PREN (Pitting Resistance) 19
7.0
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
14 to 70
Strength to Weight: Bending, points 25
15 to 45
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 17
13 to 64

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.12
Chromium (Cr), % 16 to 18
4.0 to 5.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 67.5 to 75
92.3 to 95.3
Manganese (Mn), % 5.5 to 7.5
0.2 to 0.6
Molybdenum (Mo), % 0
0.4 to 1.0
Nickel (Ni), % 3.5 to 5.5
0
Nitrogen (N), % 0.050 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0.1 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.030