EN 1.4374 Stainless Steel vs. ACI-ASTM CA40 Steel

Both EN 1.4374 stainless steel and ACI-ASTM CA40 steel are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4374 stainless steel and the bottom bar is ACI-ASTM CA40 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
310
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
10
Fatigue Strength, MPa 340
460
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 800
910
Tensile Strength: Yield (Proof), MPa 400
860

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
390
Maximum Temperature: Mechanical, °C 920
750
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1500
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 14
7.5
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.9
2.0
Embodied Energy, MJ/kg 42
28
Embodied Water, L/kg 150
100

Common Calculations

PREN (Pitting Resistance) 23
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
89
Resilience: Unit (Modulus of Resilience), kJ/m3 400
1910
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
33
Strength to Weight: Bending, points 25
27
Thermal Diffusivity, mm2/s 4.0
6.7
Thermal Shock Resistance, points 17
33

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.2 to 0.4
Chromium (Cr), % 17.5 to 18.5
11.5 to 14
Copper (Cu), % 0 to 0.4
0
Iron (Fe), % 63.5 to 67.9
81.5 to 88.3
Manganese (Mn), % 9.0 to 10
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 5.0 to 6.0
0 to 1.0
Nitrogen (N), % 0.25 to 0.32
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.3 to 0.6
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.040