EN 1.4374 stainless steel belongs to the iron alloys classification, while AWS BVPd-1 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.

For each property being compared, the top bar is EN 1.4374 stainless steel and the bottom bar is AWS BVPd-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
150
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 77
56
Tensile Strength: Ultimate (UTS), MPa 800
240

Thermal Properties

Latent Heat of Fusion, J/g 290
200
Melting Completion (Liquidus), °C 1400
1240
Melting Onset (Solidus), °C 1360
1230
Specific Heat Capacity, J/kg-K 480
310
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Density, g/cm3 7.7
11

Common Calculations

Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 29
6.1
Strength to Weight: Bending, points 25
7.9
Thermal Shock Resistance, points 17
9.8

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0.050 to 0.1
0 to 0.0050
Chromium (Cr), % 17.5 to 18.5
0
Cobalt (Co), % 0
33.9 to 36
Copper (Cu), % 0 to 0.4
0
Iron (Fe), % 63.5 to 67.9
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 9.0 to 10
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 5.0 to 6.0
0 to 0.060
Nitrogen (N), % 0.25 to 0.32
0
Palladium (Pd), % 0
64 to 66
Phosphorus (P), % 0 to 0.035
0 to 0.0020
Silicon (Si), % 0.3 to 0.6
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.0010