EN 1.4374 Stainless Steel vs. N06007 Nickel

EN 1.4374 stainless steel belongs to the iron alloys classification, while N06007 nickel belongs to the nickel alloys. They have 46% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4374 stainless steel and the bottom bar is N06007 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
38
Fatigue Strength, MPa 340
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
79
Shear Strength, MPa 550
470
Tensile Strength: Ultimate (UTS), MPa 800
690
Tensile Strength: Yield (Proof), MPa 400
260

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Mechanical, °C 920
990
Melting Completion (Liquidus), °C 1400
1340
Melting Onset (Solidus), °C 1360
1260
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 15
10
Thermal Expansion, µm/m-K 17
14

Otherwise Unclassified Properties

Base Metal Price, % relative 14
60
Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 2.9
10
Embodied Energy, MJ/kg 42
140
Embodied Water, L/kg 150
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
200
Resilience: Unit (Modulus of Resilience), kJ/m3 400
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 29
23
Strength to Weight: Bending, points 25
21
Thermal Diffusivity, mm2/s 4.0
2.7
Thermal Shock Resistance, points 17
18

Alloy Composition

Carbon (C), % 0.050 to 0.1
0 to 0.050
Chromium (Cr), % 17.5 to 18.5
21 to 23.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0 to 0.4
1.5 to 2.5
Iron (Fe), % 63.5 to 67.9
18 to 21
Manganese (Mn), % 9.0 to 10
1.0 to 2.0
Molybdenum (Mo), % 0 to 0.5
5.5 to 7.5
Nickel (Ni), % 5.0 to 6.0
36.1 to 51.1
Niobium (Nb), % 0
1.8 to 2.5
Nitrogen (N), % 0.25 to 0.32
0.15 to 0.25
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.3 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
0 to 1.0