EN 1.4378 Stainless Steel vs. SAE-AISI O6 Steel

Both EN 1.4378 stainless steel and SAE-AISI O6 steel are iron alloys. They have 67% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.4378 stainless steel and the bottom bar is SAE-AISI O6 steel.

EN 1.4378 (X6CrMnNiN18-13-3) Stainless Steel SAE-AISI O6 (T31506) Oil-Hardening Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		180

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		71

Tensile Strength: Ultimate (UTS), MPa		760 to 1130
Tensile Strength: Ultimate (UTS), MPa		670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1390
Melting Completion (Liquidus), °C		1430

Melting Onset (Solidus), °C		1350
Melting Onset (Solidus), °C		1390

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		12
Base Metal Price, % relative		2.3

Density, g/cm³		7.6
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		2.7
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		39
Embodied Energy, MJ/kg		21

Embodied Water, L/kg		150
Embodied Water, L/kg		47

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		28 to 41
Strength to Weight: Axial, points		24 to 74

Strength to Weight: Bending, points		24 to 31
Strength to Weight: Bending, points		22 to 47

Thermal Shock Resistance, points		16 to 23
Thermal Shock Resistance, points		22 to 69

Alloy Composition

Carbon (C), %		0 to 0.080
Carbon (C), %		1.3 to 1.6

Chromium (Cr), %		17 to 19
Chromium (Cr), %		0 to 0.3

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		61.2 to 69
Iron (Fe), %		94.6 to 97.7

Manganese (Mn), %		11.5 to 14.5
Manganese (Mn), %		0.3 to 1.1

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.2 to 0.3

Nickel (Ni), %		2.3 to 3.7
Nickel (Ni), %		0 to 0.3

Nitrogen (N), %		0.2 to 0.4
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.060
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.55 to 1.5

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030