EN 1.4401 Stainless Steel vs. AISI 304 Stainless Steel
Both EN 1.4401 stainless steel and AISI 304 stainless steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.4401 stainless steel and the bottom bar is AISI 304 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 270 | |
| 170 to 360 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 14 to 40 | |
| 8.0 to 43 |
| Fatigue Strength, MPa | 200 to 320 | |
| 210 to 440 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 77 |
| Shear Strength, MPa | 410 to 550 | |
| 400 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 900 | |
| 580 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 230 to 570 | |
| 230 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 950 | |
| 710 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1450 |
| Melting Onset (Solidus), °C | 1400 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 16 |
| Thermal Expansion, µm/m-K | 16 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 15 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 52 | |
| 43 |
| Embodied Water, L/kg | 150 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 26 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 190 | |
| 86 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 800 | |
| 140 to 1870 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 32 | |
| 21 to 42 |
| Strength to Weight: Bending, points | 20 to 26 | |
| 20 to 32 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.2 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 12 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.080 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 18 to 20 |
| Iron (Fe), % | 62.8 to 71.5 | |
| 66.5 to 74 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.0 to 2.5 | |
| 0 |
| Nickel (Ni), % | 10 to 13 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |