EN 1.4401 Stainless Steel vs. EN 1.4837 Stainless Steel

Both EN 1.4401 stainless steel and EN 1.4837 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4401 stainless steel and the bottom bar is EN 1.4837 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 40
6.8
Fatigue Strength, MPa 200 to 320
120
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 600 to 900
500
Tensile Strength: Yield (Proof), MPa 230 to 570
250

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Corrosion, °C 410
440
Maximum Temperature: Mechanical, °C 950
1050
Melting Completion (Liquidus), °C 1440
1390
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
20
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.8
3.7
Embodied Energy, MJ/kg 52
53
Embodied Water, L/kg 150
180

Common Calculations

PREN (Pitting Resistance) 26
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
29
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 800
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
18
Strength to Weight: Bending, points 20 to 26
18
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 13 to 20
11

Alloy Composition

Carbon (C), % 0 to 0.070
0.3 to 0.5
Chromium (Cr), % 16.5 to 18.5
24 to 27
Iron (Fe), % 62.8 to 71.5
53.4 to 63.7
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
0 to 0.5
Nickel (Ni), % 10 to 13
11 to 14
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030