EN 1.4405 Stainless Steel vs. EN 1.8932 Steel
Both EN 1.4405 stainless steel and EN 1.8932 steel are iron alloys. They have 79% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4405 stainless steel and the bottom bar is EN 1.8932 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 17 | |
20 |
Fatigue Strength, MPa | 370 | |
250 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 77 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 860 | |
600 |
Tensile Strength: Yield (Proof), MPa | 610 | |
370 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
250 |
Maximum Temperature: Mechanical, °C | 870 | |
410 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1400 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 17 | |
40 |
Thermal Expansion, µm/m-K | 11 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
8.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 13 | |
2.5 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 2.8 | |
1.7 |
Embodied Energy, MJ/kg | 39 | |
24 |
Embodied Water, L/kg | 130 | |
50 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 950 | |
370 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 31 | |
21 |
Strength to Weight: Bending, points | 26 | |
20 |
Thermal Diffusivity, mm2/s | 4.6 | |
11 |
Thermal Shock Resistance, points | 29 | |
17 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.060 |
Carbon (C), % | 0 to 0.060 | |
0 to 0.2 |
Chromium (Cr), % | 15 to 17 | |
0 to 0.3 |
Copper (Cu), % | 0 | |
0 to 0.2 |
Iron (Fe), % | 73.6 to 80.3 | |
95.5 to 98.9 |
Manganese (Mn), % | 0 to 1.0 | |
1.0 to 1.7 |
Molybdenum (Mo), % | 0.7 to 1.5 | |
0 to 0.1 |
Nickel (Ni), % | 4.0 to 6.0 | |
0 to 1.0 |
Niobium (Nb), % | 0 | |
0 to 0.050 |
Nitrogen (N), % | 0 | |
0 to 0.020 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.025 |
Silicon (Si), % | 0 to 0.8 | |
0.1 to 0.6 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.015 |
Vanadium (V), % | 0 | |
0 to 0.2 |