EN 1.4409 Stainless Steel vs. CC333G Bronze

EN 1.4409 stainless steel belongs to the iron alloys classification, while CC333G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4409 stainless steel and the bottom bar is CC333G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
13
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 78
45
Tensile Strength: Ultimate (UTS), MPa 490
710
Tensile Strength: Yield (Proof), MPa 220
310

Thermal Properties

Latent Heat of Fusion, J/g 300
230
Maximum Temperature: Mechanical, °C 990
230
Melting Completion (Liquidus), °C 1440
1080
Melting Onset (Solidus), °C 1390
1020
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
38
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 19
29
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.7
3.5
Embodied Energy, MJ/kg 52
56
Embodied Water, L/kg 160
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
75
Resilience: Unit (Modulus of Resilience), kJ/m3 120
410
Stiffness to Weight: Axial, points 14
8.0
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.1
10
Thermal Shock Resistance, points 11
24

Alloy Composition

Aluminum (Al), % 0
8.5 to 10.5
Bismuth (Bi), % 0
0 to 0.010
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0 to 0.050
Copper (Cu), % 0
76 to 83
Iron (Fe), % 61.7 to 71
3.0 to 5.5
Lead (Pb), % 0
0 to 0.030
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 3.0
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 9.0 to 12
3.7 to 6.0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.5
0 to 0.1
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.5