EN 1.4409 Stainless Steel vs. C87900 Brass

EN 1.4409 stainless steel belongs to the iron alloys classification, while C87900 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4409 stainless steel and the bottom bar is C87900 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
25
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 78
41
Tensile Strength: Ultimate (UTS), MPa 490
480
Tensile Strength: Yield (Proof), MPa 220
240

Thermal Properties

Latent Heat of Fusion, J/g 300
190
Maximum Temperature: Mechanical, °C 990
130
Melting Completion (Liquidus), °C 1440
930
Melting Onset (Solidus), °C 1390
900
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
120
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
17

Otherwise Unclassified Properties

Base Metal Price, % relative 19
24
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.7
2.7
Embodied Energy, MJ/kg 52
46
Embodied Water, L/kg 160
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
100
Resilience: Unit (Modulus of Resilience), kJ/m3 120
270
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 18
17
Thermal Diffusivity, mm2/s 4.1
37
Thermal Shock Resistance, points 11
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.15
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
63 to 69.2
Iron (Fe), % 61.7 to 71
0 to 0.4
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 0 to 2.0
0 to 0.15
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 9.0 to 12
0 to 0.5
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 1.5
0.8 to 1.2
Sulfur (S), % 0 to 0.025
0 to 0.050
Tin (Sn), % 0
0 to 0.25
Zinc (Zn), % 0
30 to 36