EN 1.4410 Stainless Steel vs. AISI 310Cb Stainless Steel

Both EN 1.4410 stainless steel and AISI 310Cb stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is AISI 310Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
190
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 24
39
Fatigue Strength, MPa 410
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
78
Shear Strength, MPa 540
390
Tensile Strength: Ultimate (UTS), MPa 850
580
Tensile Strength: Yield (Proof), MPa 600
230

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
520
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
28
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
4.8
Embodied Energy, MJ/kg 56
69
Embodied Water, L/kg 180
190

Common Calculations

PREN (Pitting Resistance) 42
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
180
Resilience: Unit (Modulus of Resilience), kJ/m3 880
140
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
20
Strength to Weight: Bending, points 26
20
Thermal Diffusivity, mm2/s 4.0
3.9
Thermal Shock Resistance, points 23
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 24 to 26
24 to 26
Iron (Fe), % 58.1 to 66.8
47.2 to 57
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
19 to 22
Niobium (Nb), % 0
0 to 1.1
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030