EN 1.4410 Stainless Steel vs. EN 1.0237 Steel

Both EN 1.4410 stainless steel and EN 1.0237 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.0237 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
20
Fatigue Strength, MPa 410
250
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
290
Tensile Strength: Ultimate (UTS), MPa 850
470
Tensile Strength: Yield (Proof), MPa 600
360

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
88
Resilience: Unit (Modulus of Resilience), kJ/m3 880
340
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
17
Strength to Weight: Bending, points 26
17
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 23
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 58.1 to 66.8
98 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.4
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.045