EN 1.4410 Stainless Steel vs. SAE-AISI H13 Steel

Both EN 1.4410 stainless steel and SAE-AISI H13 steel are iron alloys. They have 70% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is SAE-AISI H13 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
74
Tensile Strength: Ultimate (UTS), MPa 850
690 to 1820

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
29
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
8.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
9.7

Otherwise Unclassified Properties

Base Metal Price, % relative 20
6.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
4.3
Embodied Energy, MJ/kg 56
64
Embodied Water, L/kg 180
78

Common Calculations

PREN (Pitting Resistance) 42
9.9
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
25 to 65
Strength to Weight: Bending, points 26
22 to 43
Thermal Diffusivity, mm2/s 4.0
7.8
Thermal Shock Resistance, points 23
25 to 65

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.45
Chromium (Cr), % 24 to 26
4.8 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 58.1 to 66.8
88.8 to 92
Manganese (Mn), % 0 to 2.0
0.2 to 0.5
Molybdenum (Mo), % 3.0 to 4.5
1.1 to 1.8
Nickel (Ni), % 6.0 to 8.0
0 to 0.3
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0.8 to 1.2
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0
0.8 to 1.2