EN 1.4411 Stainless Steel vs. Nickel 242
EN 1.4411 stainless steel belongs to the iron alloys classification, while nickel 242 belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4411 stainless steel and the bottom bar is nickel 242.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 17 | |
| 45 |
| Fatigue Strength, MPa | 370 | |
| 300 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 78 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 820 |
| Tensile Strength: Yield (Proof), MPa | 600 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 930 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1380 |
| Melting Onset (Solidus), °C | 1410 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 17 | |
| 11 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 1.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 14 |
| Embodied Energy, MJ/kg | 41 | |
| 180 |
| Embodied Water, L/kg | 130 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 300 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 920 | |
| 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 31 | |
| 25 |
| Strength to Weight: Bending, points | 26 | |
| 21 |
| Thermal Diffusivity, mm2/s | 4.6 | |
| 3.1 |
| Thermal Shock Resistance, points | 28 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Boron (B), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.060 | |
| 0 to 0.030 |
| Chromium (Cr), % | 15 to 17 | |
| 7.0 to 9.0 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 73.1 to 79.5 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 1.5 to 2.0 | |
| 24 to 26 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 59.3 to 69 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.8 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |