EN 1.4412 Stainless Steel vs. C35000 Brass

EN 1.4412 stainless steel belongs to the iron alloys classification, while C35000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4412 stainless steel and the bottom bar is C35000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 79
40
Tensile Strength: Ultimate (UTS), MPa 490
340 to 650

Thermal Properties

Latent Heat of Fusion, J/g 300
170
Maximum Temperature: Mechanical, °C 1000
120
Melting Completion (Liquidus), °C 1450
920
Melting Onset (Solidus), °C 1400
890
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 15
120
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
26
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
29

Otherwise Unclassified Properties

Base Metal Price, % relative 20
23
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 4.1
2.7
Embodied Energy, MJ/kg 56
45
Embodied Water, L/kg 160
320

Common Calculations

Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 17
12 to 22
Strength to Weight: Bending, points 18
13 to 21
Thermal Diffusivity, mm2/s 3.9
37
Thermal Shock Resistance, points 11
11 to 22

Alloy Composition

Carbon (C), % 0 to 0.070
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
60 to 63
Iron (Fe), % 60.4 to 69
0 to 0.1
Lead (Pb), % 0
0.8 to 2.0
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 10 to 13
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
34.5 to 39.2
Residuals, % 0
0 to 0.4