EN 1.4415 Stainless Steel vs. Ductile Cast Iron
Both EN 1.4415 stainless steel and ductile cast iron are iron alloys. They have 79% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4415 stainless steel and the bottom bar is ductile cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 170 to 180 |
| Elongation at Break, % | 17 to 20 | |
| 2.1 to 20 |
| Poisson's Ratio | 0.28 | |
| 0.28 to 0.31 |
| Shear Modulus, GPa | 77 | |
| 64 to 70 |
| Shear Strength, MPa | 520 to 570 | |
| 420 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 930 | |
| 460 to 920 |
| Tensile Strength: Yield (Proof), MPa | 730 to 840 | |
| 310 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 290 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1160 |
| Melting Onset (Solidus), °C | 1420 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 490 |
| Thermal Conductivity, W/m-K | 19 | |
| 31 to 36 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 8.8 to 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.1 to 7.5 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.5 |
| Embodied Energy, MJ/kg | 51 | |
| 21 |
| Embodied Water, L/kg | 120 | |
| 43 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 160 | |
| 17 to 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1350 to 1790 | |
| 280 to 1330 |
| Stiffness to Weight: Axial, points | 14 | |
| 12 to 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 to 26 |
| Strength to Weight: Axial, points | 29 to 33 | |
| 17 to 35 |
| Strength to Weight: Bending, points | 25 to 27 | |
| 18 to 29 |
| Thermal Diffusivity, mm2/s | 5.1 | |
| 8.9 to 10 |
| Thermal Shock Resistance, points | 30 to 34 | |
| 17 to 35 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 3.0 to 3.5 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Iron (Fe), % | 75.9 to 82.4 | |
| 93.7 to 95.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 1.5 to 2.5 | |
| 0 |
| Nickel (Ni), % | 4.5 to 6.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.080 |
| Silicon (Si), % | 0 to 0.5 | |
| 1.5 to 2.8 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.5 | |
| 0 |